标题：Effects of CeO2on the mechanical property and microstructure of 3Y-TZP nanocomposite ceramic die material
作者：Zhao, Shikui ;Xu, Chonghai
作者机构：[Zhao, Shikui ;Xu, Chonghai ] School of Mechanical Engineering, Shandong Institute of Light Industry, Jinan; 250353, China;[Xu, Chonghai ] School of M 更多
会议名称：6th China International Conference on High-Performance Ceramics, CICC 2009
会议日期：August 16, 2009 - August 19, 2009
来源：Key Engineering Materials
摘要：Thermal stability and wear resistance of nanoceramic materials are excellent, so it is an ideal die material and has become one of the increasingly important topics in the field of die research. A new 3Y-TZP nanocomposite die material was prepared with hot pressing technique by using 3Y-TZP, CeO2, Al2O3and nanometer sized TiC as raw materials. Effects of CeO2on the mechanical property and microstructure of 3Y-TZP nanocomposite die material were investigated. The addition of CeO2has obvious effect on the flexural strength and fracture toughness. When the content of CeO2is 2mol%, the fracture toughness of the composite material reaches 11.22MPa·m1/2. With the increase of CeO2content, the fracture toughness becomes lower, the flexural strength and hardness first increase and then decrease. When the CeO2content is 6mol%, the maximum flexural strength reaches 866MPa. The reason for the improvement of mechanical property can be attributed to the effect of CeO2on the phase transformation of t-ZrO2and microstructure and the resulted phase transformation toughening mechanism.
© (2010) Trans Tech Publications, Switzerland.