标题:Effect of the second-step voltages on the structural and corrosion properties of silicon-calcium-phosphate (Si-CaP) coatings on Mg-Zn-Ca alloy
作者:Dou, Jinhe; Zhao, Yupeng; Lu, Lu; Gu, Guochao; Yu, Huijun; Chen, Chuanzhong
作者机构:[Dou, Jinhe; Zhao, Yupeng; Lu, Lu; Gu, Guochao; Yu, Huijun; Chen, Chuanzhong] Shandong Univ, Shenzhen Res Inst, Shenzhen 518057, Guangdong, Peoples R 更多
通讯作者:Yu, HJ;Chen, CZ;Chen, CZ;Yu, HJ;Yu, HJ
通讯作者地址:[Yu, HJ; Chen, CZ]Shandong Univ, Shenzhen Res Inst, Shenzhen 518057, Guangdong, Peoples R China;[Chen, CZ]Shandong Univ, Key Lab Liquid Solid Struct E 更多
来源:ROYAL SOCIETY OPEN SCIENCE
出版年:2018
卷:5
期:10
DOI:10.1098/rsos.172410
关键词:Si-CaP coating; second step; micro-arc oxidation; magnesium alloy;; corrosion behaviour
摘要:The applications of magnesium (Mg) alloys as biodegradable orthopedic implants are mainly restricted due to their rapid degradation rate in the physiological environment. In this study, Si-CaP micro-arc oxidation (MAO) coatings were prepared on a Mg-Zn-Ca alloy by a second-step MAO process at different voltages in order to decrease the degradation rate and increase the bioactivity of the alloy. The microstructure and morphology of the samples were characterized using XRD, FT-IR SEM and EDS. The degradation behaviours of samples were evaluated using electrochemical techniques, and immersion tests in simulated body fluid (SBF). The results indicate that the morphology of the Si-CaP coatings changed significantly with the increase in Ca/P ratio as the second-step voltage increased. The Si- CaP containing coating produced at 450 V could significantly decrease the degradation rate of Mg and caused a slow increase in pH of the SBF solution. The haemolysis test concluded that the coating C3 did not cause a haemolytic reaction. The corrosion resistance of Mg alloy was greatly improved with the Si-CaP coatings, and the Mg alloy with Si-CaP coating prepared at 450 V had the best corrosion resistance, which indicates that the Si-CaP coatings are promising for improving the biodegradation properties of Mg-based orthopedic implants. Haemolysis tests indicated that the Si-CaP coating prepared at 450 V conforms to the given standard (YY/T0127.1-93).