标题:Properties and CA4GE-engine test of TiAl-based alloy valves by permanent mold casting
作者:Sheng, Wenbin ;Ma, Chunxue ;Gu, Wanli
通讯作者:Sheng, W
作者机构:[Sheng, Wenbin ;Ma, Chunxue ;Gu, Wanli ] Department of Mechanical Engineering, Shandong University of Technology, Zibo 255049, China
会议名称:2010 International Conference on Manufacturing Engineering and Automation, ICMEA2010
会议日期:December 7, 2010 - December 9, 2010
来源:Advanced Materials Research
出版年:2010
卷:139-141
页码:557-560
DOI:10.4028/www.scientific.net/AMR.139-141.557
摘要:TiAl-based alloy valves were manufactured by combining charges compressed /vacuum arc melting (VA)/ induction skull melting (ISM) procedure with permanent mold centrifugal casting method. Microstructures, compositions and mechanical properties of as-cast and hot isostatical pressed (HIPed) valves are detected. Results show that the permanent mold centrifugal casting process obviously refines the size of grain in TiAl alloy and the tensile strength of as-cast and HIPed valves are 550MPa and 580MPa at 20°C, 370MPa and 470MPa at 815°C, respectively. As-cast specimens show ∼0% elongation at 20°C and 1∼2% at 815°C, while HIPed ones show an elongation of 1∼2% at room temperature and about 10% at 815°C. Furthermore, a 200-hour test was carried out with CA4GE-engine, which demonstrated the possibility of as-cast TiAl alloy valves for the substitution of present steel ones. © (2010) Trans Tech Publications.