标题:Analysis of PCBN tool failure mechanisms in face milling of hardened steel using damage equivalent stress
作者:Cui, Xiaobin; Guo, Jingxia; Zhao, Jun; Yan, Yanyan
作者机构:[Cui, Xiaobin; Yan, Yanyan] Henan Polytech Univ, Sch Mech & Power Engn, Jiaozuo 454003, Peoples R China.; [Guo, Jingxia] Henan Polytech Univ, Sch En 更多
通讯作者:Cui, Xiaobin
通讯作者地址:[Cui, XB]Henan Polytech Univ, Sch Mech & Power Engn, Jiaozuo 454003, Peoples R China.
来源:INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY
出版年:2015
卷:80
期:9-12
页码:1985-1994
DOI:10.1007/s00170-015-7175-2
关键词:PCBN tool; Failure mechanisms; Face milling; Hardened steel; Damage; equivalent stress
摘要:An attempt was made in the present study to apply damage mechanics to investigate the polycrystalline cubic boron nitride (PCBN) tool failure mechanisms in face milling of hardened steel. Experimental phenomenon relating to damage accumulation was found by means of analyzing the tool wear evolution and macroscale failure of the cutting tool. Damage equivalent stress was used as an indicator to reveal the tool failure mechanisms under different cutting conditions. Because of the larger value of damage equivalent stress, there was greater likelihood of tool fracture in down milling than that in up milling. Deflection of the shear angle changed the tool stress component and distribution substantially in up milling, leading to the emergence of the peak value of damage equivalent stress in spite of lower values of cutting force and tool temperature. Calculated damage equivalent stress and tool lives obtained in milling tests were compared and analyzed. It was found that damage equivalent stress can be used as an effective tool to analyze the tool failure mechanisms and assess the optimum cutting condition.