标题:The spectral selective absorbing characteristics and thermal stability of SS/TiAlN/TiAlSiN/Si3N4tandem absorber prepared by magnetron sputtering
作者:Feng, Junxiao ;Zhang, Shuo ;Lu, Yu ;Yu, Hongwen ;Kang, Limin ;Wang, Xianyang ;Liu, Zongming ;Ding, Haicheng ;Tian, Yun ;Ouyang, Jun
作者机构:[Feng, Junxiao ;Zhang, Shuo ;Lu, Yu ;Kang, Limin ;Wang, Xianyang ;Tian, Yun ;Ouyang, Jun ] Key Lab. for Liquid-Solid Structure Evolution and Processin 更多
通讯作者:Ouyang, Jun
来源:Solar Energy
出版年:2015
卷:111
页码:350-356
DOI:10.1016/j.solener.2014.11.005
摘要:Spectrally selective TiAlN/TiAlSiN/Si3N4multilayer coatings were deposited on stainless steel (SS) plate using a reactive direct current magnetron sputtering technique. In this tandem absorber system, TiAlN, TiAlSiN and Si3N4act as the main absorbing layer, the semi-absorbing layer and the antireflection layer, respectively. An average absorptance (α) of 0.938 and emittance (Ε) of 0.099 were achieved in coatings prepared under optimized conditions, which exhibit a fine-grained morphology and an amorphous microstructure as evidenced by SEM and XRD analysis, respectively. Absorptance and emittance data, as well as Raman spectra were collected for coatings exposed to different levels of thermal stresses (2h in air @200°C, 300°C, 400°C, 500°C, 600°C). These heat treated coatings showed negligible to small degradations in their selective absorbing capabilities as compared with the as-grown ones. There was no significant change of the coatings in their morphology or composition after the heat treatments, as evidenced by the SEM and Raman spectra analysis, respectively. The spectral selectivity of the coatings remained stable after a heat-treatment at 272°C in air for 300h.
© 2014 Elsevier Ltd.
收录类别:EI
资源类型:期刊论文
TOP