标题:The Microalloying Effects in Cu-Based Bulk Metallic Glasses
作者:Li Jie.Yue;Jin Sheng.Han;Kun.Xie
作者机构:Shandong University of Science and Technology;Shandong University of Science and Technology;Shandong University of Science and T
来源:Materials Science Forum
出版年:2011
期:688
页码:407-412
DOI:10.4028/www.scientific.net/MSF.688.407
关键词:Thermal Stability,Glass Forming Ability (GFA),Cu-Based Bulk Metallic Glass,Polarization Curve,Corrosion Resistance
摘要:The glassy alloy rods of Cu50Zr43Al7, (Cu50Zr43Al7)100-xYx(x=2,5) and (Cu50Zr43Al7)100-xAgx(x=6,7) with diameters of 3.0 mm were prepared by copper mold suction casting method. The influence of adding Ag and Y to Cu50Zr43Al7 metallic glass on glass formation ability (GFA) and thermal stability was studied by means of X-ray diffraction analysis (XRD) and differential scanning calorimetry (DSC). The results show that Ag and Y appropriate micro-addition enhance the glass formation ability and thermal stability of the Cu-Zr-Al metallic glass. The effect of Ag is better than that of Y. The addition of Ag causes a increase of the reduced glass transition temperature (Trg) of (Cu50Zr43Al7)100-xAgx alloy from 0.618 at 0 at.% Ag to 0.628 at 7 at.% Ag. The width of the supercooled liquid region of Cu43Zr43Al7Ag7 glassy alloy increases about 25K compared with that of Cu50Zr43Al7, and the γ value of Cu43Zr43Al7Ag7 reaches 0.433. The electrochemical corrosion behaviors of Cu50Zr43Al7, (Cu50Zr43Al7)100-xYx(x=2,5) and (Cu50Zr43Al7)100-xAgx(x=6,7) metallic glasses in 3.5% NaCl solution were investigated by potentiodynamic polarization method. It is found that corrosion resistance of all amorphous alloys is better than that of the corresponding crystalline alloys. The Ag and Y micro-addition improve corrosion resistance of Cu50Zr43Al7 metallic glass. The corrosion current density of Cu43Zr43Al7Ag7 metallic glass decreases 1~2 orders of magnitude compared with that of Cu50Zr43Al7.
资源类型:期刊论文
TOP