标题：Fabrication of porous platelike LiFePO4/C cathode materials via hydrothermal process
作者：Yu, Weiyan ;Wu, Lili ;Zhao, Jinbo ;Zhang, Yanpeng ;Li, Gaozeng ;Gai, Hongde
作者机构：[Yu, Weiyan ;Wu, Lili ;Zhao, Jinbo ;Zhang, Yanpeng ;Li, Gaozeng ] Key Laboratory for Liquid-Solid Structural Evolution and Process of Materials, Minis 更多
摘要：The porous platelike LiFePO4/C particles were synthesized through an in situ hydrothermal process. Citric acid or glucose was added as carbon source to conduct carbon coating and ascorbic acid served as reducing agent. The material synthesized with citric acid shows the particle size of 2-3μm with a refined carbon coating layer and delivers a discharge capability of 152.7mAhg-1at 0.1C while the material prepared with glucose demonstrates an average size of about 2μm with a thin carbon coating layer and exhibits a discharge capacity of 153.4mAhg-1at 0.1C. The latter has a smaller voltage difference between the charge and discharge plateaus. Both materials have negligible capability fading at 0.1C after 50 cycles, possessing excellent cycle stability. © 2012 Elsevier B.V.