标题:Effect of high temperature oxidation on cemented carbide during brazing
作者:Xu, Deng-Qiang ;Li, Hui-Qi ;Li, Min ;Wang, Shu-Feng ;Chi, Jing
作者机构:[Xu, Deng-Qiang ;Li, Hui-Qi ;Li, Min ;Wang, Shu-Feng ;Chi, Jing ] School of Materials Science and Engineering, Shandong University of Science and Tech 更多
通讯作者:Li, Hui-Qi
来源:Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment
出版年:2015
卷:36
期:1
页码:75-79
摘要:The oxidation behavior of YG-11C cemented carbide heating at 900, 950, 1000 was investigated, and the performance of oxidation of carbide bit during the brazing was measured. The results show that oxidation of cemented carbide occurs in 10 min when the temperature is above 900, the hard phase WC and binder phase Co are oxidized into WO3 and CoWO4. Deformation and mass gain occur when the cemented carbide is oxidized, and the higher the temperature is the more serious the oxidation behavior is, and the more obvious deformation and mass gain is. The microstructure of carbide bit becomes loose and porous after surface oxidation during brazing at high temperature, and the hardness and wear-resistance decrease. ©, 2015, Editorial Office of Transactions of Materials and Heat Treatment. All right reserved.
收录类别:EI
资源类型:期刊论文
TOP