标题：A study on corrosion behaviors of laser cladded Fe-Cr-Ni coating in as-cladded and machined conditions
作者：Zhang, Peirong; Liu, Zhanqiang; Su, Guosheng; Du, Jin; Zhang, Jingjie
作者机构：[Zhang, Peirong; Su, Guosheng; Du, Jin; Zhang, Jingjie] Qilu Univ Technol, Shandong Acad Sci, Sch Mech & Automot Engn, Jinan 250353, Shandong, Peoples 更多
通讯作者：Zhang, PR;Liu, ZQ;Zhang, Peirong
通讯作者地址：[Zhang, PR]Qilu Univ Technol, Shandong Acad Sci, Sch Mech & Automot Engn, Jinan 250353, Shandong, Peoples R China;[Liu, ZQ]Shandong Univ, Sch Mech Eng 更多
来源：MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION
关键词：corrosion resistance; Fe-Cr-Ni coating; laser cladding; potentiodynamic; polarization; turning
摘要：This paper investigates the effect of turning process on surface quality and corrosion behaviors of laser cladded coatings on the 1045 steel. Corrosion resistance of the 1045 steel is improved by laser cladded Fe-Cr-Ni coatings. The as-cladded coating behaves nobler and more resistant to corrosion compared to the 1045 steel substrate. By using turning as a finish process, surface roughness R-a of the laser cladded coating is decreased to 0.517 mu m to meet the surface roughness requirement (i.e., R-a <= 0.8 mu m) of a single-telescopic hydraulic column. Also, surface defects including laps, cavities, and adhered material particles occur on the cladded coatings after machining. The machined coatings exhibit comparable polarization resistance compared to the as-cladded condition, and the polarization resistance of the machined surface increases with feed rate increasing. The corrosion pits show sensitivity on feed marks induced by machining. This concentrated distribution of corrosion pits is a result of the fluctuation of local electron work function (EWF), which promotes the formation of local corrosion cells in adjacency to feed marks.