标题：Aminopropyl-modified silica as cross-linkers of polysiloxane containing gamma-chloropropyl groups for preparing heat-curable silicone rubber
作者：Dong, Fuying; Ma, Depeng; Feng, Shengyu
作者机构：[Dong, Fuying; Ma, Depeng; Feng, Shengyu] Shandong Univ, Key Lab Special Funct Aggregated Mat, Jinan 250100, Peoples R China.; [Dong, Fuying; Ma, De 更多
通讯作者：Feng, SY;Feng, SY
通讯作者地址：[Feng, SY]Shandong Univ, Key Lab Special Funct Aggregated Mat, Jinan 250100, Peoples R China;[Feng, SY]Shandong Univ, Key Lab Colloid & Interface Chem 更多
关键词：Aminopropyl-modified silica; Polysiloxane containing gamma-chloropropyl; groups; Cross-linking; Mechanical property; Thermal stability
摘要：A series of aminopropyl-modified silica (APS) with different amine contents was prepared and, subsequently, used as cross-linkers of polysiloxane containing gamma-chloropropyl groups (CPPS) to prepare heat curable silicone rubber (MCSR). The dispersion of APS in polysiloxane matrix was studied by scanning electron microscopy. The curing characteristics, mechanical and thermal properties of the MCSR were analyzed by a rheometer, mechanical testing and thermal gravimetric analysis (TGA), respectively. The effects of the silica (TS530) content and the molar ratio of APS/CPPS on the curing characteristics were studied. The influence of the amounts of TS530 and APS, and the kind of APS, on the comprehensive mechanical properties of MCSR is discussed. The optimized conditions to prepare MCSR were obtained as follows: the amount of TS530, 55 parts per hundreds of polysiloxane in weight; the molar ratio of [N-H]/[gamma-chloropropyl], 1.5: 1; and the amount of amino groups on the surface of APS, 0.65 mmol/g. Additionally, TGA results show that MCSR has high thermal stability. (C) 2016 Elsevier Ltd. All rights reserved.