标题:Microstructure and wear properties of TiC-VC reinforced iron based hardfacing layers
作者:Wang XH;Zhang M;Zou ZD;Qu SY
通讯作者:Wang, XH
作者机构:[Wang, X.H] Key Lab. for Liquid Structure and Heredity of Materials, Shandong University, Jinan 250061, China;[ Zhang, M] School of Mechanical Enginee 更多
来源:Materials Science and Technology: MST: A publication of the Institute of Metals
出版年:2006
卷:22
期:2
页码:193-198
DOI:10.1179/174328406X81595
关键词:TiC-VC particles;Fe based hardfacing layer;microstructure;wear properties;COMPOSITE;ELECTRODE
摘要:TiC-VC reinforced Fe based hardfacing layers were obtained by shielded manual arc welding (SMAW) of which H08A rare electrodes were coated by different amounts of ferrotitanium (FeTi), ferrovanadium (FeV) and graphite. The microstructure of the hardfacing layers was investigated by means of scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electron probe microanalysis (EPMA). The thermodynamics and effect of elements on the carbides were also discussed. It was shown that TiC-VC carbides could be formed during arc welding. The composition and amount of flux evidently affect the microstructure and properties of the coatings. Good crack resistance and higher hardness of the harfacing layer could be obtained, while the amounts of graphite, FeTi and FeV were controlled within a range of 8-10%, 15-18% and 8-12% respectively. TiC-VC reinforced Fe based hardfacing layers possess much greater wear resistance and a smaller friction coefficient than 1045 steel substrate.