标题:MnO2 based sandwich structure electrode for supercapacitor with large voltage window and high mass loading
作者:Zhang, Yue; Yuan, Xiaomin; Lu, Weibang; Yan, Yushan; Zhu, Junwu; Chou, Tsu-Wei
作者机构:[Zhang, Yue; Zhu, Junwu] Nanjing Univ Sci & Technol, Key Lab Soft Chem & Funct Mat, Minist Educ, Nanjing 210094, Jiangsu, Peoples R China.; [Zhang, 更多
通讯作者:Zhu, JW;Chou, TW
通讯作者地址:[Zhu, JW]Nanjing Univ Sci & Technol, Key Lab Soft Chem & Funct Mat, Minist Educ, Nanjing 210094, Jiangsu, Peoples R China;[Chou, TW]Univ Delaware, Dep 更多
来源:CHEMICAL ENGINEERING JOURNAL
出版年:2019
卷:368
页码:525-532
DOI:10.1016/j.cej.2019.02.206
关键词:Large voltage window; High mass loading; Sandwich structure; Flexible;; Supercapacitor
摘要:The need for developing energy storage devices with high energy and power densities has motivated tremendous effort in the research of supercapacitors. Major challenges still exist in improving the working voltage window and specific capacitance of the devices. Here, we report a systematic effort in achieving remarkable supercapacitor performance. Firstly, a flexible CNT film/double side carbon tape/CNT film@MnO2 (CDC@MnO2) positive electrode with a large voltage window of 0-1.2 V was fabricated via a facial one-step water bath process. The large interfacial area created by the CDC sandwich structure enabled a high MnO2 mass loading up to 6.6 mg cm(-2), resulting in a high area capacitance of 1.1 F cm(-2) at a current density of 1 mA cm(-2). Secondly, inspired by the superior electrochemical performance of the CDC@MnO2 positive electrode, a CDC@Fe2O3 film with area capacitance up to 339.1 mF cm(-2) was fabricated as the negative electrode. Thirdly, a flexible asymmetric supercapacitor was successfully assembled which possesses a large voltage window of 0-2.1 V, a high volume capacitance of 6.8 F cm(-3), and a high energy density of 4.1 mWh cm(-3) at the power density of 22.3 mW cm(-3).