标题:Composition dependent cation distribution in ZnxGa2O3+xnanocrystals
作者:Li, Nannan ;Zhu, Pengfei ;Duan, Xiulan
作者机构:[Li, Nannan ;Zhu, Pengfei ;Duan, Xiulan ] State Key Laboratory of Crystal Materials, Institute of Crystal Materials, Shandong University, Jinan; 25010 更多
通讯作者:Duan, Xiulan
来源:Physica B: Condensed Matter
出版年:2018
卷:530
页码:290-294
DOI:10.1016/j.physb.2017.11.047
摘要:ZnxGa2O3+x(0.8 ≤ x ≤ 1.1) nanocrystals with the size of 15–30 nm were prepared by the sol-gel method. The effect of composition (Zn/Ga ratio) on the distribution of Zn2+and Ga3+ions was studied using X-ray photoelectron spectroscopy (XPS). Both of these cations occupied tetrahedral sites as well as octahedral sites of spinel structure in the studied samples. Octahedral Ga3+ions are dominant and the as-synthesized samples are partially inverse spinel-structure. The fraction of tetrahedral Ga3+ions was calculated to be 0.07–0.16, and increased with Zn/Ga ratio increasing. The inverse parameter (two times the fraction of Ga3+in the tetrahedral sites) increases from 0.14 to 0.32 when x value increases from 0.8 to 1.1. The EPR and emission spectra indicated that oxygen vacancies formed in the nanocrystals. The emission intensity of the peak due to oxygen vacancies decreased with increasing Zn/Ga ratio, indicating the decreasing of the concentration of oxygen vacancy.
© 2017 Elsevier B.V.
收录类别:EI
资源类型:期刊论文
TOP