标题:Texture development in a twin roll cast and warm rolled ZK60 magnesium alloy
作者:Chen, Hongmei; Yu, Huashun; Kang, Suk Bong; Min, Guanghui
通讯作者:Chen, H.
作者机构:[Chen, Hongmei] Jiangsu Univ Sci & Technol, Sch Mat Sci & Engn, Zhenjiang 212003, Peoples R China.; [Yu, Huashun; Min, Guanghui] Shandong Univ, Mini 更多
会议名称:Magnesium Technology Symposium 2010
会议日期:FEB 14-18, 2010
来源:MAGNESIUM TECHNOLOGY 2010
出版年:2010
页码:559-562
关键词:warm rolling; microstructure; texture; pole figure; ZK60 alloy
摘要:The effect of rolling conditions on the microstructure and texture development of twin roll cast ZK60 alloy strips was investigated. Microstructure and texture were measured on specimens subjected to rolling experiments of different thickness reduction per pass. Texture of ZK60 Mg alloy sheets were evaluated by X-ray diffraction method in this study. The (10 (1) over bar0), (0002) pole figures were measured. Tensile test was performed to show the influence of the per pass thickness reduction on mechanical properties. The microstructure of ZK60 alloy sheets consisted of fibrous structure with elongated grains and a relatively density of shear bands along the rolling direction which were warm rolled at 350 degrees C with 10%, 30% and 50% thickness reduction per pass. Dynamic recrystallization could be found during the warm rolling process with different per pass thickness reduction. Grain refinement was found to occur during the warm rolling process, producing a finer grain size of which was warm rolled with 50% reduction in single pass rolling at 350 degrees C. This could result in better mechanical properties.
收录类别:CPCI-S;EI;SCOPUS
资源类型:会议论文;期刊论文
原文链接:https://www.scopus.com/inward/record.uri?eid=2-s2.0-77952384271&partnerID=40&md5=ae38cca4845bbceeb7fd47950d7db791
TOP