标题:Formability prediction of AL7020 with experimental and numerical failure criteria
作者:Yue, Z. M.; Badreddine, H.; Dang, T.; Saanouni, K.; Tekkaya, A. E.
作者机构:[Yue, Z. M.] Shandong Univ, Sch Mech Elect & Informat Engn, Weihai, Peoples R China.; [Badreddine, H.; Saanouni, K.] Univ Technol Troyes, ICD LASMIS 更多
通讯作者:Yue, Z.M.
通讯作者地址:[Yue, ZM]Shandong Univ, Sch Mech Elect & Informat Engn, Weihai, Peoples R China.
来源:JOURNAL OF MATERIALS PROCESSING TECHNOLOGY
出版年:2015
卷:218
页码:80-88
DOI:10.1016/j.jmatprotec.2014.11.034
关键词:Formability; Forming limit curves; Constitutive equations; Ductile; damage
摘要:The formability of aluminum alloy sheet metal is a key issue in its design, analysis and operation of manufacturing processes. The conventional forming limit diagram (FLD) which evaluates the principal strains at failure is often used to quantify the formability limits. Due to the sensitivity of the FLD to the strain paths, the forming limit stress diagram (FLSD) based on principal stresses is shown to be more efficient. In contrast, a fully coupled behavior-damage models are recently proposed, which allow to predict the strain localization and the failure occurrence based on appropriates fully coupled constitutive equations describing the main physical phenomena involved. In this work a fully coupled constitutive equations taking into account the mixed nonlinear isotropic and kinematic hardenings fully coupled with the isotropic ductile damage is used. The microcracks closure is added to affect the equivalent plastic strain at fracture in a large range of stress states. Various tests are conducted to test the formability of aluminum alloy AL7020. The three different methods (FLD, FLSD and the fully coupled model) are identified and validated separately. With the help of Nakazima tests and cross-section deep drawing tests, the quality of the three failure criteria for AL7020 are compared and demonstrated with the investigations of the simulation results. (C) 2014 Elsevier B.V. All rights reserved.