标题:The effect of SiC particles added in electroless Ni-P plating solution on the properties of composite coatings
作者:Zhang SS;Han KJ;Cheng L
作者机构:[Zhang, S] Institute for Thermal Science and Technology, Shandong University, Jinan, 250061, China;[ Han, K] School of Mechanical Engineering, Shandon 更多
通讯作者:Han, K
通讯作者地址:[Han, KJ]Shandong Univ, Sch Mech Engn, Jinan 250061, Peoples R China.
来源:Surface & Coatings Technology
出版年:2008
卷:202
期:12
页码:2807-2812
DOI:10.1016/j.surfcoat.2007.10.015
关键词:electroless Ni-P plating solution;SiC particles;composite coatings;corrosion resistance;CAVITATION EROSION BEHAVIOR;DEPOSITS;HARDNESS
摘要:To verify the relationship between the properties of composite coatings prepared on Q235 steel and the SiC content of electroless Ni-P-SiC composite coatings, systematic experiments with varied SiC contents and surfactants have been conducted. The experimental results indicated the approximate linear relation between the SiC content and the hardness of composite coatings. With the increasing of SiC content, wear resistance increases correspondingly. In particular, the effect of SiC content on the corrosion resistance of Ni-P-SiC composite coatings immersed in different corrosive solutions (i.e. 5% H2SO4, 20% NaOH and 3.5% NaCl) is explored, followed by a comparative analysis of the corrosion resistance between Ni-P and Ni-P-SiC coatings. Corrosion test indicates that NaOH solution makes no differences in the corrosion resistance between Ni-P coatings and electroless Ni-P-SiC composite coatings, both being uncorroded. Exposed to NaCl solution, the corrosion resistance of electroless Ni-P-SiC composite coatings decreases gradually with the increasing of SiC content in coatings. In H2SO4 solution, the corrosion resistance of coatings increases initially and decreases afterwards with the sustained increasing of SiC content in coatings, and the optimized corrosion resistance is obtained at a SiC content of 9.41 wt.%. Finally, a competent electroless Ni-P-SiC composite plating process producing a high wear resistance and sound corrosion resistance of the coatings is obtained. (C) 2007 Elsevier B.V. All rights reserved.