标题:Response to “Comments on ‘Selective evolution of secondary γ′ precipitation in a Ni-based single crystal superalloy both in the γ matrix and at the dislocation nodes’”
作者:Xiang S.; Long H.; Mao S.; Liu Y.; Wei H.; Zhang J.; Shen Z.; Zhang H.;等 更多
作者机构:[Xiang, S] Institute of Microstructure and Property of Advanced Materials, Beijing University of Technology, Beijing, 100024, China;[ Long, H] Institu 更多
通讯作者:Mao, S(scmao@bjut.edu.cn)
通讯作者地址:[Mao, S] Institute of Microstructure and Property of Advanced Materials, Beijing University of TechnologyChina;
来源:Scripta Materialia
出版年:2017
卷:129
页码:104-106
DOI:10.1016/j.scriptamat.2016.10.013
关键词:Ni-based superalloys; Precipitates
摘要:In their comment (Scripta Mater. (2016)), Cormier et al. raised questions on the findings reported in our earlier publication (Acta Mater. (2016) of the formation of 2nd γ′d and 2nd γ′γ precipitates in a Ni-based single crystal superalloy during creep testing at elevated temperatures, and suggested that the 2nd γ′d particles were mere observations of surface protuberances of the primary γ′ rafts and that the 2nd γ′γ precipitates were possibly formed during cooling after the creep test. To clarify these, we conducted new experiments, and present the new evidence and our responses to the points raised in this short communication. © 2016 Elsevier Ltd