标题:Microstructure and high-temperature mechanical properties of Nb-silicide based in-situ composites
作者:Liu Dong-ming; Jiang Rong-li; Sha Jiang-bo
通讯作者:Sha, JB
作者机构:School of Materials Science and Engineering, South Campus, Shandong University, Ji\'nan 250061, China;School of Materials Science
会议名称:Beijing International Materials Week
会议日期:JUN 25-30, 2006
来源:中国有色金属学会会刊(英文版)
出版年:2006
卷:16
页码:2022-2025
关键词:Nb-15W-18Si-xHf alloys;niobium;silicide;microstructure;strength;fracture toughness
摘要:Nb-15W-18Si-xHf (x = 0, 5, 10 and 15, mole fraction, %) alloys were prepared by arc melting and then homogenized at1 750 ℃ for 50 h. The microstructure and mechanical behaviors, such as Vickers hardness, fracture toughness, room- and high- temperature strength of the alloys were investigated. The microstructure of the annealed Nb-15W-18Si-xHf alloys is composed of large primary NbSS dendrite and fine eutectic mixture of NbSS and M5Si3 silicide. Both the hardness and the fracture toughness show an increase tendency at room temperature with increase of Hf content. The 0.2% compressive yield strength, σ0.2 of the alloys with5 %Hf and 10%Hf are larger than 960 MPa at 1 200 ℃, and about 500 MPa even at 1 500 ℃.
收录类别:CPCI-S;SCIE
WOS核心被引频次:2
资源类型:会议论文;期刊论文
TOP